Bioactivity, osteogenicity and mechanical properties of α-tricalcium phosphate (α-TCP) based phosphates cements can be improved by adding tricalcium silicate (C3S); however, the addition of C3S delays the precipitation and growth of calcium deficient hydroxyapatite (CDHA). Thus, the aim of this work was the study of in situ setting reaction of α-TCP/C3S composite bone cement under high energy X-ray generated by a synchrotron source within the first 72h. The results showed that the addition of C3S induces the precipitation of nanosized CDHA at early times depending on the added content. Calculated crystallite sizes showed that the higher the content of C3S, the smaller the crystal size at the beginning of the precipitation. These results are different from those obtained by conventional XRD method, suggesting that the proposed technique is a powerful tool in determining the composition and extent of reaction of CPCs surfaces in real time.

There are evidences considering the effectiveness of Si on enhancing biological properties of calcium phosphates; however, there are not many works relating to the Si-alpha-TCP bone cement. The influence of silicon doping on the properties of Α-TCP cement was analyzed. Si-TCP was obtained by a solid state reaction employing CaCO3, CaHPO4 and CaSiO3 and powder was analyzed by XRD, FTIR, XRF and BET specific area. Cement samples were analyzed for their surface of fracture morphology, mechanical resistance and SBF bioactivity. Cement mechanical resistance was not satisfactory for biomedical application; nonetheless, sample's surface was coated by an apatite layer after immersion in SBF. Notwithstanding, to ensure that silicon is the element responsible for increasing the material's bioactivity it is necessary to evaluate the in vivo performance of the bone cement obtained in this work.

The addition of tricalcium silicate (C3S) to apatite cements results in an increase of bioactivity and improvement in the mechanical properties. However, adding large amounts raises the local pH at early stages, which retards the precipitation of hydroxyapatite and produces a loss of mechanical strength. The introduction of Pozzolanic materials in cement pastes could be an effective way to reduces basicity and enhance their mechanical resistance; thus, the effect of adding silica on the chemical, mechanical and biological properties of α-tricalcium phosphate/C3S cement was studied. Adding silica produces a reduction in the early pH and a decrease in setting times; nevertheless, the presence of more calcium silicate hydrate (C-S-H) delays the growth of hydroxyapatite crystals and consequently, reduces early compressive strength. The new formulations show a good bioactivity, but higher cytotoxicity than traditional cements and additions higher than 2.5% of SiO2 cause a lack of mechanical strength and an elevated degradability.

The effect of the method of sterilization on the physical, chemical and mechanical properties of a new bone repairing material was studied. The material was obtained by thermal hydrolysis of beta-tricalcium phosphate/orthophosphoric acid cement and was composed of calcium deficient hydroxyapatite, octacalcium phosphate (OCP), and beta-tricalcium phosphate. Partial decomposition of the OCP was observed after sterilization for the three methods. Decomposition increased to the following sequence of sterilization methods: ethylene oxide; autoclaving; dry oven. On the other hand, mechanical strength decreased with regard to non sterilized material in the sterilization sequence: ethylene oxide; dry oven; autoclaving. The compressive strength was 8.5 ± 1.0; 9.0 ± 1.2; 8.2 ± 0.8 and 6.5 ± 1.0 MPa, whereas diametral tensile strength was 2.1 ± 0.3; 2.5 ± 0.1; 1.9 ± 0.9 and 1.6 ± 0.3 for the material sterilized by ethylene oxide, dry oven, and autoclaving, respectively. Several compositional and microstuctural changes were detected after dry heat and autoclave sterilization. Ethylene oxide sterilization had lesser effect on the chemical composition and strength than dry heat and autoclaving.